X60钢大压下变形后的微观组织

宗云, 赵莉萍, 麻永林, 王宝峰

文章导航 > 钢铁钒钛 > 2006 > 27(2): 57-62,68

宗云, 赵莉萍, 麻永林, 王宝峰. X60钢大压下变形后的微观组织[J]. 钢铁钒钛, 2006, 27(2): 57-62,68.

引用本文:

宗云, 赵莉萍, 麻永林, 王宝峰. X60钢大压下变形后的微观组织[J]. 钢铁钒钛, 2006, 27(2): 57-62,68.

Zong Yun, Zhao Liping, Ma Yonglin, Wang Baofeng. Microstructure of X60 Steel after Heavy-deformation[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(2): 57-62,68.

Citation:

Zong Yun, Zhao Liping, Ma Yonglin, Wang Baofeng. Microstructure of X60 Steel after Heavy-deformation[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(2): 57-62,68.

宗云, 赵莉萍, 麻永林, 王宝峰. X60钢大压下变形后的微观组织[J]. 钢铁钒钛, 2006, 27(2): 57-62,68.

引用本文:

宗云, 赵莉萍, 麻永林, 王宝峰. X60钢大压下变形后的微观组织[J]. 钢铁钒钛, 2006, 27(2): 57-62,68.

Zong Yun, Zhao Liping, Ma Yonglin, Wang Baofeng. Microstructure of X60 Steel after Heavy-deformation[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(2): 57-62,68.

Citation:

Zong Yun, Zhao Liping, Ma Yonglin, Wang Baofeng. Microstructure of X60 Steel after Heavy-deformation[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(2): 57-62,68.

X60钢大压下变形后的微观组织

1. 山东轻工业学院机械工程系, 山东济南 250100;
2. 内蒙古科技大学材料科学与工程学院, 内蒙古包头 014010

基金项目:

内蒙古高校科学研究项目(NJ04025)。

作者简介:
宗云(1974-),女,山东临朐人,硕士,主要从事金属微观组织研究。

中图分类号: TG142.1
计量
- 文章访问数: 24
- HTML全文浏览量: 4
- PDF下载量: 1
- 被引次数: 0
出版历程
- 收稿日期: 2005-12-10
- 网络出版日期: 2023-12-06

Microstructure of X60 Steel after Heavy-deformation

1. Shandong Institute of Light Industry, Jinan 250100, Shandong, China;
2. University of Science and Technology Inner Mongolia, Baotou 014010, Mongolia, China

摘要:
X60钢单道次和双道次大压下模拟变形分别在f130二辊实验轧机和Gleeble- 1500热模拟机上进行。变形后,对热模拟试样的组织进行分析发现:变形试样的组织主要是多边形的铁素体和微量的类珠光体,在铁素体晶粒边界和晶粒内部以及位错线上有许多较细小的碳氮化物弥散析出,尺寸约为十几纳米,呈不规则分布或点列状分布。
- X60钢 /
- 变形工艺 /
- 微观组织 /
- 碳氮化物 /
- 热压缩试验
Abstract:
Single-pass deformation and double-pass hot compression test of X60 steel were tested respectively on the f130 trial two-rollers mill and the Gleeble-1500 thermo-mechanical simulator.The results show the microstructure of deformed sample consists of main polygon ferrite and a little pearlite.There are a lot of dispersed Nb(C,N) precipitates in the ferrite,among the boundaries and on the dislocations.The diameter of the precipitate is about 10 nm or so,which distributed with the form of point-liner or irregular.
- X60 steel /
- deformation process /
- microstructure /
- carbonitride /
- hot compression test

参考文献(0)

资源附件(0)

WeChat

点击查看大图

计量

文章访问数: 24
HTML全文浏览量: 4
PDF下载量: 1
被引次数: 0

/

下载: 全尺寸图片幻灯片

分享

用微信扫码二维码

分享至好友和朋友圈

返回

本系统由北京仁和汇智信息技术有限公司开发

x 关闭永久关闭

《钢铁钒钛》期刊新投审稿
系统上线公告