由工业V₂O₅制取VO₂薄膜

杨绍利, 徐楚韶, 陈厚生, 胡再勇

文章导航 > 钢铁钒钛 > 2002 > 23(2): 7-10

杨绍利, 徐楚韶, 陈厚生, 胡再勇. 由工业V2O5制取VO2薄膜[J]. 钢铁钒钛, 2002, 23(2): 7-10.

引用本文:

杨绍利, 徐楚韶, 陈厚生, 胡再勇. 由工业V₂O₅制取VO₂薄膜[J]. 钢铁钒钛, 2002, 23(2): 7-10.

YANG Shao-li, XU Chu-shao, CHEN Hou-sheng, HU Zai-yong. PREPARATION OF VO2 THIN FILMS FROM INDUSTRIAL V2O5[J]. IRON STEEL VANADIUM TITANIUM, 2002, 23(2): 7-10.

Citation:

YANG Shao-li, XU Chu-shao, CHEN Hou-sheng, HU Zai-yong. PREPARATION OF VO₂ THIN FILMS FROM INDUSTRIAL V₂O₅[J]. IRON STEEL VANADIUM TITANIUM, 2002, 23(2): 7-10.

杨绍利, 徐楚韶, 陈厚生, 胡再勇. 由工业V2O5制取VO2薄膜[J]. 钢铁钒钛, 2002, 23(2): 7-10.

引用本文:

杨绍利, 徐楚韶, 陈厚生, 胡再勇. 由工业V₂O₅制取VO₂薄膜[J]. 钢铁钒钛, 2002, 23(2): 7-10.

YANG Shao-li, XU Chu-shao, CHEN Hou-sheng, HU Zai-yong. PREPARATION OF VO2 THIN FILMS FROM INDUSTRIAL V2O5[J]. IRON STEEL VANADIUM TITANIUM, 2002, 23(2): 7-10.

Citation:

YANG Shao-li, XU Chu-shao, CHEN Hou-sheng, HU Zai-yong. PREPARATION OF VO₂ THIN FILMS FROM INDUSTRIAL V₂O₅[J]. IRON STEEL VANADIUM TITANIUM, 2002, 23(2): 7-10.

由工业V₂O₅制取VO₂薄膜

1. 重庆大学材料科学与工程学院, 重庆 400044;
2. 攀枝花钢铁研究院, 四川攀枝花 617000

作者简介:
杨绍利(1963-),男,副教授,辽宁黑山人,重庆大学博士研究生,主要从事氧化钒薄膜、纳米材料和催化剂研究

中图分类号: TB43,O614.51
计量
- 文章访问数: 26
- HTML全文浏览量: 6
- PDF下载量: 2
- 被引次数: 0
出版历程
- 收稿日期: 2002-02-05
- 网络出版日期: 2023-12-06

PREPARATION OF VO₂ THIN FILMS FROM INDUSTRIAL V₂O₅

1. College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China;
2. Panzhihua Iron & Steel Research Institute, Panzhihua 617000, Sichuan, China

摘要: 以工业V₂O₅为原料,采用N₂热分解法在普通玻璃和石英玻璃衬底上制备VVO₂薄膜,在自制的电阻-温度测量装置上测量VO₂薄膜的电阻随温度的变化。结果表明:VO₂薄膜具有明显电阻突变特性,其相变达到了1.5~2.0个数量级,相变温度约为35℃;VO₂薄膜的主要成分是二氧化钒,同时含有少量其它的钒化合物。
- V₂O₅ /
- VO₂ /
- 薄膜 /
- 热分解 /
- M-S相变
Abstract: Using industrial V₂O₅ as raw material,VO₂ thin films are preparied by thermal decomposition method on common glass and quartz glass.The resistance changing of VO₂ thin films with temperature has been tested by temperature-resistance measurement device designed by authors.The results are shown as follow:VO₂ thin film has obvious suddenly changing properties,and the suddenly changing of resistance reaches 10 ^1.5~2.0.The changing temperature is about 35℃.The major composition of VO₂ thin films is vanadium dioxide,and a little other chemical compounds of vanadium.
- V₂O₅ /
- VO₂ /
- thin film /
- thermal decomposition /
- M-S phase transition

参考文献(0)

资源附件(0)

WeChat

点击查看大图

计量

文章访问数: 26
HTML全文浏览量: 6
PDF下载量: 2
被引次数: 0

/

下载: 全尺寸图片幻灯片

分享

用微信扫码二维码

分享至好友和朋友圈

返回

本系统由北京仁和汇智信息技术有限公司开发

x 关闭永久关闭

《钢铁钒钛》期刊新投审稿
系统上线公告