草酸氧钒热分解制备纳米VO₂及粉体表征

林华, 邹建, 李庆

文章导航 > 钢铁钒钛 > 2006 > 27(1): 55-58,63

林华, 邹建, 李庆. 草酸氧钒热分解制备纳米VO2及粉体表征[J]. 钢铁钒钛, 2006, 27(1): 55-58,63.

引用本文:

林华, 邹建, 李庆. 草酸氧钒热分解制备纳米VO₂及粉体表征[J]. 钢铁钒钛, 2006, 27(1): 55-58,63.

Lin Hua, Zou Jian, Li Qing. Preparation and characterization of VO2 Nano- powder by Thermal Decomposing VOC2O4·H2O[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(1): 55-58,63.

Citation:

Lin Hua, Zou Jian, Li Qing. Preparation and characterization of VO₂ Nano- powder by Thermal Decomposing VOC₂O₄·H₂O[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(1): 55-58,63.

林华, 邹建, 李庆. 草酸氧钒热分解制备纳米VO2及粉体表征[J]. 钢铁钒钛, 2006, 27(1): 55-58,63.

引用本文:

林华, 邹建, 李庆. 草酸氧钒热分解制备纳米VO₂及粉体表征[J]. 钢铁钒钛, 2006, 27(1): 55-58,63.

Lin Hua, Zou Jian, Li Qing. Preparation and characterization of VO2 Nano- powder by Thermal Decomposing VOC2O4·H2O[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(1): 55-58,63.

Citation:

Lin Hua, Zou Jian, Li Qing. Preparation and characterization of VO₂ Nano- powder by Thermal Decomposing VOC₂O₄·H₂O[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(1): 55-58,63.

草酸氧钒热分解制备纳米VO₂及粉体表征

林华¹,
邹建²,
李庆¹

1. 西南大学材料科学与工程学院, 重庆 400715;
2. 西南大学化学化工学院, 重庆 400715

基金项目:

西南大学青年基金(SWNUQ2004003)，教育部科学技术重点项目(105144)。

作者简介:
林华(1976-),男,硕士,主要从事纳米材料研究。

中图分类号: TB383
计量
- 文章访问数: 17
- HTML全文浏览量: 3
- PDF下载量: 1
- 被引次数: 0
出版历程
- 收稿日期: 2005-10-11
- 网络出版日期: 2023-12-06

Preparation and characterization of VO₂ Nano- powder by Thermal Decomposing VOC₂O₄·H₂O

1. School of Materials Science and Engineering, Southwest University, Chongqing, 400715;
2. School of Chemistry and Chemical Engineering, Southwest University, Chongqing, 400715

摘要: 研究了一种在350℃分解草酸氧钒前驱体（VOC₂O₄·H₂O,草酸还原工业V₂O₅粉的产物）来制备纳米VO₂粉末的方法。采用TG-DSC、XRD、TEM及电阻—温度仪等测试手段对所得粉末进行了测试分析,实验结果表明:所得VO₂粉末呈结晶态,组分单一,粒径为80~120 nm,相变温度为68.5℃,电阻突变量约3个数量级。
- 纳米VO₂粉末 /
- 工业V₂O₅粉 /
- 草酸氧钒 /
- 热分解
Abstract: A method of synthesizing VO₂ nano-powder by decomposing VOC₂O₄·H₂O（which was made from commercial V₂O₅ powder deoxidized by oxalic acid） in vacuum oven pipe at 350 ℃ was developed.The powder was characterized by means of thermal analysis（TG-DSC）,X-ray diffraction spectroscopy（XRD）,transmission electron microscope（TEM） and resistance-thermometer.The results show that the powder is crystallized,the component is only VO₂,the average particle size is 80～120 nm,its phase transition temperature is 68.5 ℃,and its resistance abrupt change reaches three magnitudes.
- VO₂ nano- powder /
- commercial V₂O₅ powder /
- VOC₂₄·H₂O /
- thermal decomposition

参考文献(0)

资源附件(0)

WeChat

点击查看大图

计量

文章访问数: 17
HTML全文浏览量: 3
PDF下载量: 1
被引次数: 0

/

下载: 全尺寸图片幻灯片

分享

用微信扫码二维码

分享至好友和朋友圈

返回

本系统由北京仁和汇智信息技术有限公司开发

x 关闭永久关闭

《钢铁钒钛》期刊新投审稿
系统上线公告