Technology of High Efficient Slab Caster at PISCO
-
摘要: 简述了攀钢板坯连铸高效化生产技术及其应用效果。通过研究开发适应高拉速要求的连铸保护渣、结晶器冷却制度和钢水温度控制制度,连铸拉速达到1.30~1.80 m/min;通过应用钢包渣改性、精炼工艺优化和高粘度连铸保护渣,IF钢冷轧板卷条痕缺陷率由10.97%降至1%以内;通过合理分配两台板坯铸机功能,推广应用中包快换水口,减少LF工序钢水加热时间和提高RH连续处理能力等技术,铸机作业率由平均89.39%增至92.96%。为攀钢2008年上半年板坯产量达154万t提供了重要的技术支撑。Abstract: Technologies of high efficient slab caster and its application effect at PISCO(Panzhihua Iron & Steel Co.) were presented.The casting speed was increased to the range between 1.30 m/min and 1.80 m/min owing to developing reasonable mold flux,primary cooling scheme and molten steel temperature control.The rate of sliver defect on cold-rolled sheet was decreased from 10.97% to 1% due to adjusting compositions and performance of steel slag,optimizing refining process,and designing high viscosity flux.Meanwhile,the mean operating rate of slab caster was increased from 89.39% to 92.96% benefit from reasonable distributing function between two slab casters,applying quick exchanging for nozzle,reducing reheating time of molten steel at LF,and improving production capacity of RH.These achievements have provided important technology supports for PISCO to obtain 154 million tons product of continuously cast slab in half a year of 2008.
-
Key words:
- slab continuous casting /
- high efficient continuous casting /
- mold flux /
- primary cooling /
- slab quality
点击查看大图
计量
- 文章访问数: 18
- HTML全文浏览量: 4
- PDF下载量: 1
- 被引次数: 0