Producing Refractory Raw Materials with Vanadium Iron Slag
-
摘要: 以钒铁渣、菱镁矿为主要原料,采用共磨、机压成形、高温烧成的生产工艺,生产出了主晶相为刚玉、尖晶石,体积密度大于3.0 g/cm3,吸水率小于1.5%,耐火度大于1 790℃的人工合成耐火原料,可替代高铝矾土、烧成尖晶石等耐火原料用于不烧砖、浇注料等产品中,实现工业固体废弃物的二次资源化及高附加值利用。Abstract: Using vanadium iron slag and magnesite as main raw material,appling co-grinding,machine press forming,high temperature firing processes,a kind of synthetic refractory raw materials can be produced,which has main phases of corundum and spinel,and it's density greater than 3.0 g/cm3,the rate of water absorption less than 1.5%,and refractoriness more than 1 790℃.It can be used in unfired bricks,castable and other products instead of bauxite and firing spinel and other refractory raw materials.In this process,vanadium iron slag can be used as secondary resource and can realize high value utilization.