帘线钢精炼工艺技术研究

曾建华,  陈永,  王新华,  姜敏,  杨森祥,  张敏,  潘红

downloadPDF
文章导航 > 钢铁钒钛  > 2015 >  36(6): 94-100
曾建华, 陈永, 王新华, 姜敏, 杨森祥, 张敏, 潘红. 帘线钢精炼工艺技术研究[J]. 钢铁钒钛, 2015, 36(6): 94-100. doi: 10.7513/j.issn.1004-7638.2015.06.018
引用本文: 曾建华, 陈永, 王新华, 姜敏, 杨森祥, 张敏, 潘红. 帘线钢精炼工艺技术研究[J]. 钢铁钒钛, 2015, 36(6): 94-100. doi: 10.7513/j.issn.1004-7638.2015.06.018
shu
Zeng Jianhua, Chen Yong, Wang Xinhua, Jiang Min, Yang Senxiang, Zhang Min, Pan Hong. Study on Refining Technology of High Quality Cord Steel Production[J]. IRON STEEL VANADIUM TITANIUM, 2015, 36(6): 94-100. doi: 10.7513/j.issn.1004-7638.2015.06.018
Citation: Zeng Jianhua, Chen Yong, Wang Xinhua, Jiang Min, Yang Senxiang, Zhang Min, Pan Hong. Study on Refining Technology of High Quality Cord Steel Production[J]. IRON STEEL VANADIUM TITANIUM, 2015, 36(6): 94-100. doi: 10.7513/j.issn.1004-7638.2015.06.018
shu

帘线钢精炼工艺技术研究

doi: 10.7513/j.issn.1004-7638.2015.06.018

  • 1. 攀钢集团研究院有限公司, 钒钛资源综合利用国家重点实验室, 四川 攀枝花 617000;

  • 2. 北京科技大学冶金与生态工程学院, 北京 100083;

  • 3. 攀钢集团攀枝花钢钒有限公司, 四川 攀枝花 617062

详细信息

  • 中图分类号: TF76,TF769

Study on Refining Technology of High Quality Cord Steel Production

  • 1. Pangang Group Research Institute Co., Ltd., State Key Laboratory of Vanadium and Titanium Resources Comprehensive Utilization, Panzhihua 617000, Sichuan, China;

  • 2. University of Science and Technology Beijing, Beijing 100083, China;

  • 3. Pangang Group Panzhihua Steel and Vanadium Co., Ltd., Panzhihua 617062, Sichuan, China

    摘要
  • 摘要: 针对高品质帘线钢对钢中夹杂物组分及钢液洁净度的严格要求,系统地开展了钢包顶渣组成和精炼工艺流程的研究。理论研究结果和生产实践表明,精炼过程将钢包顶渣二元碱度(CaO/SiO2)控制在1.0左右,渣中Al2O3含量控制在6%~8%,可以将夹杂物基本控制在低熔点塑性区域;与DeS-LD-LF-Ar-CC工艺相比,采用DeS-LD-LF-RH-CC生产工艺可以在实现夹杂物塑性化转变的同时进一步降低钢中T[O]、[N],提高钢液洁净度。所生产的帘线钢吨钢断丝率平均为0.47次/t,疲劳寿命在2万次以上。
    Abstract: In order to meet the strict requirements of inclusion and cleanliness for high quality cord steel,top slag composition and refining process had been studied through predication and industrial practice.The results show that the inclusions can meet the requirements of plasticity at lower melting temperature when the tap slag basicity (CaO/SiO2) and Al2O3 content are controlled at about 1.0 and in the range of 6%~8%,respectively. Compared with the process of DeS-LD-LF-Ar-CC,the process of DeS-LD-LFRH-CC can lead to inclusion meeting requirements of plasticity and further reducing content of T[O] and [N],and thus improve the cleanliness. The average wire broken ratio of cord steel products is 0.47 time per ton and the fatigue lifetimes reached over 20,000 cycles.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  49
  • HTML全文浏览量:  4
  • PDF下载量:  10
  • 被引次数: 0
出版历程
  • 收稿日期:  2015-07-09

目录

    /

    返回文章
    返回

    地址：四川省攀枝花市东区桃源街90号攀钢集团攀枝花钢铁研究院有限公司技术发展研究中心《钢铁钒钛》编辑部（617000）

    邮政编码：617000联系电话：0812-3380763,3380539,3380764蜀ICP备05030275号-5川公网安备 51040202000080号

    版权所有：攀钢集团攀枝花钢铁研究院有限公司技术发展研究中心《钢铁钒钛》编辑部

    E-mail alert RSS

    本系统由 北京仁和汇智信息技术有限公司 开发 

    x 关闭 永久关闭

    《钢铁钒钛》期刊新投审稿
    系统上线公告