Study on Dealkalization Capacity of BF Slag with Low Titanium Content
-
摘要: 针对某钢厂高炉低钛渣系的排碱能力进行试验,研究w(CaO)/w(SiO2)、w(MgO)、w(Al2O3)、w(TiO2)以及初始碱含量对炉渣排碱能力的影响。结果表明:随炉渣w(CaO)/w(SiO2)的提高,炉渣中w(MgO)和初始碱含量的增加,高炉渣的排碱能力都逐渐降低;随炉渣中w(Al2O3)的提高,炉渣的排碱能力逐渐增强;炉渣的排碱能力随w(TiO2)的增加有小幅度的降低。建议高炉生产应适当的降低炉渣w(CaO)/w(SiO2),炉渣的w(CaO)/w(SiO2)应保持在1.05到1.10左右;适当降低w(MgO),炉渣w(MgO)含量保持在7%~8%左右;适当增加w(Al2O3),降低w(TiO2);减少碱金属的入炉量,降低高炉碱负荷。Abstract: According to the dealkalization capacity of blast furnace(BF) slag with low titanium content in an integrated iron and steel company were tested and analyzed, the effects of wCaO/wSiO2,wMgO,wAl2O3,wTiO2 and initial alkali content on dealkalization capacity of BF slag were studied.The results show that:with the increase of wCaO/wSiO2,wMgO and initial alkali content,the dealkalization capacity of BF slag decreases gradually.With the increase of wAl2O3,the dealkalization capacity of BF slag increa-ses.The dealkalization capacity increases slowly with the increase of wTiO2.wCaO/wSiO2 and wMgOshould be properly reduced in BF production,wCaO/wSiO2 and wMgOshould be kept at 1.05~1.10 and 7%~8%.wAl2O3can be appropriately increased,wTiO2can be decreased appropriately.The amount of alkali entering into the BF should be reduced,in order to reduce the degree of harmness to the BF.
-
Key words:
- blast furnace /
- BF slag /
- alkali /
- imported ore /
- dealkalization capacity
点击查看大图
计量
- 文章访问数: 6
- HTML全文浏览量: 1
- PDF下载量: 1
- 被引次数: 0