Development and Welding Thermal Simulation Test of the Normalizing Type 460 MPa Steel for Container
-
摘要: 以C-Mn-Si为基础,通过VN微合金化,添加适量镍的成分设计思路,采取控轧和正火工艺,生产出低屈强比高强韧容器用钢板。对正火板进行焊接热模拟试验,结果表明:随着t8/5时间的增加,即热输入的提高,焊接热影响区的硬度和冲击值下降,铁素体含量和晶粒尺寸是主要影响因素;热输入为12.36~14.27 kJ/cm时,可以获得良好CGHAZ性能。Abstract: A C-Mn-Si base chemistry with Ni addition and V-N microalloying had been designed for producing low yield strength high toughness steel plate via control rolling and normalizing process.The resulted steel plate had been conducted welding thermal simulation test.Welding test results show that with the increase of t8/5 time,ie,the increase of heat input,the hardness and impact value of HAZ decreases.Microstructure observation indicates that volume fraction and grain size of ferriteare the main reason for the deterioration of CGHAZ performance.Good CGHAZ performance can be achieved at 12.36~14.27 kJ/cm of heat input.
-
Key words:
- container steel /
- VN microalloying /
- normalizing /
- welding heat simulation
点击查看大图
计量
- 文章访问数: 16
- HTML全文浏览量: 6
- PDF下载量: 1
- 被引次数: 0