高铬钒渣浸出行为研究

doi: 10.7513/j.issn.1004-7638.2019.02.002

1. 长江师范学院化学化工学院, 重庆 408100;
2. 重庆大学化学化工学院, 重庆 400030

基金项目:

重庆市基础研究与前沿探索（一般）项目（cstc2018jcyjAX0018），长江师范学院人才引进项目（2017KYQD117）。

详细信息

通讯作者:
彭浩(1990-),男,讲师,通讯作者,研究方向为化工过程强化,绿色资源化工。E-mail:cqupenghao@126.com。

中图分类号: TF841.3
计量
- 文章访问数: 31
- HTML全文浏览量: 9
- PDF下载量: 2
- 被引次数: 0
出版历程
- 收稿日期: 2018-12-23
- 网络出版日期: 2023-12-02

Leaching of Vanadium and Chromium from High Chromium Vanadium Slag

1. College of Chemistry and Chemical Engineering, Yangtze Normal University, Chongqing 408100, China;
2. College of Chemistry and Chemical Engineering, Chongqing University, Chongqing 400030, China

摘要

摘要: 高铬钒渣中钒和铬主要以尖晶石结构存在，难以直接溶出。试验以CaF₂和MnO₂作为助浸剂，对高铬钒渣的酸性湿法浸出过程进行强化。研究了CaF₂用量、MnO₂用量和反应时间等反应参数对钒铬浸出率的影响。试验结果表明：在酸性条件下，低价钒和铬难以直接溶出，浸出率只有38.47%和14.72%。CaF₂的加入可以破坏高铬钒渣表面的硅氧化合物结构，使得低价的钒和铬释放出来，与体系中的MnO₂反应被氧化溶出。适当延长反应时间，使各反应物充分接触，可以提高钒和铬的浸出率。在CaF₂和MnO₂的辅助浸出过程中，钒和铬的浸出率可以提高到62.08%和29.56%。
- 高铬钒渣 /
- 浸取 /
- MnO₂ /
- CaF₂ /
- 钒 /
- 铬 /
- 浸出率
Abstract: Vanadium and chromium are hard to be leached out directly from the high chromium vanadium slag since they co-exist in spinel in the slag.CaF₂ and MnO₂ were applied to intensify the leaching process of vanadium and chromium from high chromium vanadium slag.The dosage of CaF₂,the dosage of MnO₂ and reaction time on the leaching efficiency of vanadium and chromium were investigated.The results indicate that the vanadium and chromium in low valence are hard to be leached out in acid condition,with the leaching efficiency of vanadium and chromium at 38.47% and 14.72%,respectively.The addition of CaF₂ could destroy the Si-O structure and the vanadium and chromium in low valence can be released out,and then oxidized by MnO₂.The leaching efficiency of vanadium and chromium increase with increase of the reaction time.The leaching efficiency of vanadium and chromium can be respectively increased to 62.08% and 29.56% with CaF₂ and MnO₂ intensifying the leaching process.
- high chromium vanadium slag /
- leaching /
- MnO₂ /
- CaF₂ /
- vanadium /
- chromium /