Influence of Alloying Elements on the Precipitation Phase and High-temperature Endurance Property of Blade Steel KT5331
-
摘要: 热力学软件及试验研究合金元素对KT5331钢析出相的影响。结果表明:M23C6析出温度、析出量由C元素决定,钢中Cr、Mo元素含量对M23C6析出温度影响较大。Laves相析出量由W含量决定。根据合金元素对析出相的影响规律,分析了合金元素对KT5331钢高温持久性能的影响。结果表明:降低C含量,Cr、W元素含量在下限,Mo元素含量在中上限,对KT5331钢高温持久性能有利。Abstract: The influence of alloying elements on equilibrium precipitation phases of KT5331 were studied by Factsage software and experiment.The results show that the amount of M23C6 carbide is determined by C content in steel.The fluctuation of Cr,Mo content in steel has effect on precipitation temperature of M23C6.The amount of Laves phase is determined by the W content.Based on the influence of alloying elements on the precipitated phase,the influence of alloying elements on the high-temperature endurance property of KT5331 steel was analyzed.The results showed that in order to achieve high temperature durability of KT5331 steel,the C content should be reduced and the Cr and W elements are at the lower level,and the Mo element content is at the middle or upper limit.
-
Key words:
- KT5331 /
- M23C6 /
- Laves phase /
- high-temperature endurance property
点击查看大图
计量
- 文章访问数: 14
- HTML全文浏览量: 6
- PDF下载量: 1
- 被引次数: 0