Study on inclusions and microstructure of 55SiCrA spring steel wire rod
-
摘要: 利用光学显微镜(OM)、扫描电镜(SEM-EDS)以及Factsage热力学软件对国内外弹簧用线材夹杂物与组织进行了研究。结果表明：国内外3家钢厂弹簧钢线材在显微组织、中心偏析、脱碳层厚度、晶粒度等方面相差不大；国内Y厂弹簧钢线材中发现有1级D类夹杂物以及1.5级Ds类夹杂，而国外H厂和国内B厂相对较好，均未出现Ds类夹杂物。国外H厂弹簧钢夹杂物数量最少，尺寸最小，最大尺寸仅3.4 μm且可变形比例近100%；然而国内弹簧钢线材夹杂物数量多、尺寸大且不可变形。国内Y厂线材夹杂物平均Al2O3、MgO含量较高，国内B厂发现有纯Al2O3夹杂物。此外，国内钢厂需进一步合理控制钢水、精炼渣成分以及提高耐材质量并合理选用耐火材料，来强化夹杂物的改性和脱除。Abstract: Inclusions and microstructure of 55SiCrA spring steel wire rod were studied by means of OM, SEM-EDS and Factsage software. The results show that the microstructure, central segregation, thickness of decarburized layer and grain size of spring steel wire rod in the three plants at home and abroad are almost the same. Moreover, the level 1 D-type inclusions and the level 1.5 Ds-type inclusions are found in domestic steel Y (DSY), however, no Ds-type inclusions are found in foreign steel H (FSH) and domestic steel B (DSB). The number of inclusions in spring steel of FSH is the least and their size is the smallest, the maximum size is only 3.4 μm, and the deformable ratio is nearly 100%; however, the inclusions in spring steel wire rod of DSY and DSB are large in number and size, and are not deformable. The average contents of Al2O3 and MgO are higher in inclusions of DSY, and pure Al2O3 inclusions are found in the wire rod of DSB. In addition, for domestic steel mills it is necessary to further control the composition of molten steel and refined slag, improve the quality of refractory materials and select refractory materials reasonably to enhance the modification and removal of inclusions.
-
Key words:
- spring steel /
- wire rod /
- microstructure /
- inclusion
-
图 1 弹簧钢的显微组织及脱碳层
Figure 1. Microstructure and decarbonization of the tested spring steel
图 5 国内B厂弹簧钢中纯Al2O3夹杂物形貌
Figure 5. Morphologies of pure Al2O3 inclusions in the tested spring steel of DSB
图 6 国外H厂弹簧钢中高SiO2含量夹杂物沿轧制方向的形态
Figure 6. Morphologies of the high SiO2 content inclusions along rolling direction in the tested spring steel of FSH
表 1 弹簧钢的夹杂物级别与显微组织
Table 1. Inclusion grading and microstructure of the tested spring steel
厂家 显微组织 中心偏析 脱碳层厚度/μm 晶粒度级别 夹杂物级别 全脱碳层 总脱碳层 国外H厂 S+P+F 0 0 38 7 A0.5，B0.5，C1，D0.5 国内Y厂 S+P+F 0 0 56 8 A0.5，B0.5，C0.5，D1，DS1.5 国内B厂 S+P+F 0 0 44 8 A0.5，B0.5，C0.5，D0.5e 
下载: 导出CSV
表 2 弹簧钢线材夹杂物成分、尺寸、类型及盘条酸溶铝含量
Table 2. Inclusion composition, size, type and acid soluble aluminum content of the tested spring steel
编号 夹杂物成分/% 平均Al2O3
含量/%平均MgO
含量/%夹杂物尺寸
(长×宽)/μm夹杂物
类型盘条Als
含量×106Al2O3 MgO SiO2 MnO CaO 国外H厂 20.93 16.96 52.55 9.56 11.8 0.5 23.3×2.5 MnO-SiO2-Al2O3 (-MgO) 3 国内Y厂 50.9 22.5 14.04 12.56 23.6 24.5 4.7×4.7 CaO-SiO2-Al2O3-MgO 23 国内B厂 92.17 1.84 3.18 2.81 89.6 4.4 4.1×3.1 Al2O3-SiO2-CaO (-MgO) 10
下载: 导出CSV
-
[1] Canale L C F, Penha R N, Totten G E, et al. Overview of factors contributing to steel spring performance and failure[J]. International Journal of Microstructure and Materials Properties, 2007,2(3−4):262−309. [2] Lyu S, Ma X, Huang Z, et al. Inclusion characterization and formation mechanisms in spring steel deoxidized by silicon[J]. Metallurgical and Materials Transactions B, 2019,50(2):732−747. doi: 10.1007/s11663-019-01505-3 [3] Wu Xuexing, Sun Haibo, Yu Dahua. Production practice of high quality automobile suspension spring steel 55SiCr[J]. Jiangxi Metallurgy, 2016,36(2):13−16. (吴学兴, 孙海波, 余大华. 高品质汽车悬架弹簧钢55SiCr生产工艺实践[J]. 江西冶金, 2016,36(2):13−16. doi: 10.3969/j.issn.1006-2777.2016.02.004 [4] Meng Yaoqing, Guo Xiaopei, Zhao Lei, et al. Study on exogenous inclusions in rotary bending fatigue fracture of Si-killed spring steel 55SiCr[J]. Journal of Iron and Steel Research, 2018,30(12):977−982. (孟耀青, 郭晓培, 赵垒, 等. 硅脱氧弹簧钢55SiCr旋转弯曲疲劳断口中外来夹杂物的研究[J]. 钢铁研究学报, 2018,30(12):977−982. [5] Meng Yaoqing, Wang Kunpeng, Zheng Yongrui. Analysis of sources of inclusions induced fatigue failure in 1950 MPa-grade spring steel 55SiCrA[J]. Journal of Iron and Steel Research, 2017,29(10):859−864. (孟耀青, 王昆鹏, 郑永瑞. 1950 MPa级弹簧钢55SiCrA疲劳断口夹杂物来源分析[J]. 钢铁研究学报, 2017,29(10):859−864. [6] （殷瑞钰. 钢的质量现代进展[M]. 北京: 冶金工业出版社, 1995.）Ying Ruiyu.Progress of quality of steel[M]. Beijing: Metallurgical Industry Press, 1995. [7] Hu Yang, Chen Weiqing, Han Huaibin, et al. Quality contrast of domestic and overseas spring steel wire rod for valve spring[J]. Steelmaking, 2015,31(6):47−52. (胡阳, 陈伟庆, 韩怀宾, 等. 国内外气门簧用弹簧钢线材质量对比[J]. 炼钢, 2015,31(6):47−52. [8] Cui Huaizhou, Chen Weiqing, Cao Changfa. Analysis of banded structure in wire rod for tire cord steel[J]. Heat Treatment of Metals, 2011,36(6):41−45. (崔怀周, 陈伟庆, 曹长法. 帘线钢盘条带状组织的分析[J]. 金属热处理, 2011,36(6):41−45. [9] Karihara K. Production technology of wire rod for high tensile strength steel cord[J]. Kobelco Technology Review, 2011,30:62−65. [10] Maede S, Soejima T, Saito T, et al. Shape Control of inclusions in wire rods for high tensile cord by refining with synthetic slag[C]//Steelmaking Conference Proceedings.Warrendale: Iron and Steel Society of USA, 1989, 77: 379−385. [11] (殷雪. 汽车悬架弹簧钢非金属夹杂物塑性化控制研究[D]. 北京: 北京科技大学, 2018.)Yin Xue. Investigation on non-metallic inclusion plasticization control for automotive suspension spring steel[D]. Beijing: University of Science and Technology Beijing, 2018. [12] Peng Hongbing, Tang Yao. Quality comparison of the domestic and foreign high carbon steel cord wire[J]. Heat Treatment of Metals, 2019,44(12):44−48. (彭红兵, 唐尧. 国内外帘线用高碳钢线材质量对比[J]. 金属热处理, 2019,44(12):44−48. [13] Wang Kunpeng, Jiang Min, Wang Xinhua, et al. Progress of control technology of inclusions in steel for tyre cord and saw wire[J]. Special Steel, 2016,37(2):26−31. (王昆鹏, 姜敏, 王新华, 等. 钢帘线和切割丝用钢夹杂物控制技术的进展[J]. 特殊钢, 2016,37(2):26−31. doi: 10.3969/j.issn.1003-8620.2016.02.008 -