铁素体区保温对钒微合金化HRB500显微组织和力学性能的影响

吕远 亓海全 眭文杰 石代敏 谢国庆

吕远, 亓海全, 眭文杰, 石代敏, 谢国庆. 铁素体区保温对钒微合金化HRB500显微组织和力学性能的影响[J]. 钢铁钒钛, 2021, 42(1): 160-163. doi: 10.7513/j.issn.1004-7638.2021.01.026
引用本文: 吕远, 亓海全, 眭文杰, 石代敏, 谢国庆. 铁素体区保温对钒微合金化HRB500显微组织和力学性能的影响[J]. 钢铁钒钛, 2021, 42(1): 160-163. doi: 10.7513/j.issn.1004-7638.2021.01.026
Lv Yuan, Qi Haiquan, Sui Wenjie, Shi Daimin, Xie Guoqing. Effect of ferrite thermal insulation on microstructure and mechanical properties of vanadium microalloyed HRB500 steel rebar[J]. IRON STEEL VANADIUM TITANIUM, 2021, 42(1): 160-163. doi: 10.7513/j.issn.1004-7638.2021.01.026
Citation: Lv Yuan, Qi Haiquan, Sui Wenjie, Shi Daimin, Xie Guoqing. Effect of ferrite thermal insulation on microstructure and mechanical properties of vanadium microalloyed HRB500 steel rebar[J]. IRON STEEL VANADIUM TITANIUM, 2021, 42(1): 160-163. doi: 10.7513/j.issn.1004-7638.2021.01.026

铁素体区保温对钒微合金化HRB500显微组织和力学性能的影响

doi: 10.7513/j.issn.1004-7638.2021.01.026
基金项目: 有色金属及材料加工新技术教育部重点实验室开放基金资助(2019KF-13);广西建筑新能源与节能重点实验室(桂科能19-J-21-13)。
详细信息
    作者简介:

    吕远(1994—),男,硕士,主要从事金属材料研究,E-mail:lvyuan328@qq.com

    通讯作者:

    亓海全(1981—),男,副教授,博士,主要从事材料成形与热处理研究,E-mail: 22664798@qq.com

  • 中图分类号: TF76, TG156.2

Effect of ferrite thermal insulation on microstructure and mechanical properties of vanadium microalloyed HRB500 steel rebar

  • 摘要: 通过Gleeble3500对HRB500进行了奥氏体区形变+铁素体区保温的热模拟压缩试验,研究了铁素体区保温工艺对HRB500组织和性能的影响。结果表明,试样加热到980 ℃保温15 min,进行80%压下之后,随着铁素体区保温温度的降低,珠光体组织逐渐碎化,铁素体出现少量针状结构,但硬度未随之发生规律性改变;在保温工艺中,700 ℃×15 min保温时获得了最高硬度(HV)300,较直接冷却试样提高了30,这可归于碳化钒的析出强化,进一步延长保温时间硬度显著降低,可知保温过程中晶粒的粗化抵消了碳化钒的第二相强化效果。由试验数据可以推测,常规热轧生产的HRB500并未充分利用VC的第二相强化,在轧后冷床上进行700 ℃×10~15 min的保温作业,可望实现该钢10 MPa以上的强度增量。
  • 图  1  试样原始组织和热压缩后显微组织

    Figure  1.  Microstructure of as-cast and after heat compression samples

    图  2  试样在750 ℃保温的显微组织:(a)5 min;(b)15 min;(c)30 min

    Figure  2.  Microstructure of the sample held at 750 ℃:(a)5 min,(b)15 min,(c)30 min

    图  3  试样在700 ℃保温的显微组织:(a)5 min;(b)15 min;(c)30 min

    Figure  3.  Microstructure of the sample held at 700 ℃:(a)5 min,(b)15 min,(c)30 min

    图  4  试样在650 ℃保温的显微组织:(a)5 min;(b)15 min;(c)30 min

    Figure  4.  Microstructure of the sample held at 650 ℃:(a)5 min,(b)15 min;(c)30 min

    图  5  保温温度对材料硬度的影响

    Figure  5.  Effect of holding temperature on material hardness

    图  6  保温时间对材料硬度的影响

    Figure  6.  Effect of holding time on material hardness

    表  1  钢的化学成分与轧态硬度(HV)

    Table  1.   Chemical compositions and hardness of as-hot rolled steel

    化学成分/%平均硬度
    CSiMnSPV
    0.20~0.25 0.35~0.80 1.46~1.60 ≤0.04 ≤0.04 0.08~0.02 280
    下载: 导出CSV
  • [1] (周大伟, 李元廷. V-Nb微合金化HRB500钢筋的试制[C]//第二届宝钢学术年会, 2006: 422−424.)

    Zhou Dawei, Li Yuanting. Trial production of V-Nb micro-alloyed HRB500 reinforced bar[C]. Baosteel BAC 2006, 2006: 422−424.
    [2] Lin Bingsong. Analysis on rolling and process improvement of high-strength reinforced HRB500 steel with vanadium microalloying[J]. China High-Teach Enterprises, 2013,(8):37−38. (林炳松. 钒微合金化HRB500高强度钢筋轧制与工艺改进探析[J]. 中国高新技术企业, 2013,(8):37−38.
    [3] Zhao Liang, Zhang Chaohui, Ju Jiantao, et al. Comparison experiment and research on HRB500 reinforced bars produced by adding V-N alloy and V-Fe alloy[J]. Materials & Heat Treatment, 2007,36(8):35−37. (赵亮, 张朝晖, 巨建涛, 等. 钒铁与钒氮合金生产HRB500钢筋的对比试验研究[J]. 材料热处处理, 2007,36(8):35−37.
    [4] Yang Caifu, Zhang Yongquan, Liu Shuping. Strengthening mechanism in V-N micro-alloyed reinforcing bar steels[J]. Iron and Steel, 2001,36(5):55−57. (杨才福, 张永权, 柳书平. 钒氮微合金化钢筋的强化机制[J]. 钢铁, 2001,36(5):55−57. doi: 10.3321/j.issn:0449-749X.2001.05.015
    [5] OHMORIA, O IK, KAWABATA F, et al. Effect of VN precipitates on formation of grain boundary and intragranular ferrite in a high N-V bearing steel[J]. Journal of the Iron and Steel Institute of Japan, 1998,84(7):797−803.
    [6] (王芳丽. 微合金化钢筋中V、Nb析出行为研究[D]. 重庆: 重庆大学, 2016.)

    Wang Fangli. Study on precipitation behaviors of V and Nb in microalloyed steel bars[D]. Chongqing: Chongqing University, 2016.
    [7] Wang Andong, Wang Junyu, Tian Linmao. Precipitation law of V (C, N) in austenite of vanadium microalloyed steel[J]. Materials for Mechanical Engineering, 2016,40(8):23−26. (王安东, 王骏宇, 田林茂. V (C, N)在含钒微合金钢奥氏体中的析出规律[J]. 机械工程材料, 2016,40(8):23−26. doi: 10.11973/jxgccl201608006