Zhang Shulin, Li Minjiao, Li Zhiyuan. Preparation of Mesoporous TiO2 and Its Photocatalytic Decolorization Performance[J]. IRON STEEL VANADIUM TITANIUM, 2013, 34(2): 36-38,45. doi: 10.7513/j.issn.1004-7638.2013.02.008
Citation:
Zhang Shulin, Li Minjiao, Li Zhiyuan. Preparation of Mesoporous TiO2 and Its Photocatalytic Decolorization Performance[J]. IRON STEEL VANADIUM TITANIUM, 2013, 34(2): 36-38,45. doi: 10.7513/j.issn.1004-7638.2013.02.008
Zhang Shulin, Li Minjiao, Li Zhiyuan. Preparation of Mesoporous TiO2 and Its Photocatalytic Decolorization Performance[J]. IRON STEEL VANADIUM TITANIUM, 2013, 34(2): 36-38,45. doi: 10.7513/j.issn.1004-7638.2013.02.008
Citation:
Zhang Shulin, Li Minjiao, Li Zhiyuan. Preparation of Mesoporous TiO2 and Its Photocatalytic Decolorization Performance[J]. IRON STEEL VANADIUM TITANIUM, 2013, 34(2): 36-38,45. doi: 10.7513/j.issn.1004-7638.2013.02.008
Mesoporous TiO2 was prepared by a sol-gel method with the assistance of cetyl trimethyl ammonium bromide(CTAB).Then the activity of the photocatalyst so produced for photocatalytic decolorization of methyl orange(MO)solution was evaluated,and the photocatalyst was characterized with BET specific surface.The results indicate that with the ratio of nCTAB to nTBOT at 1:4 and calcination temperature at 450℃,mesoporous TiO2 can be obtained.In addition,the activity of TiO2 prepared in our experiments for photocatalytic decolorization of methyl orange is two times that of the TiO2 commercially available.