Zhang Yubo, Miao Jingguo, Li Zhihong, Huang Wanxia. Effects of Interlayer Annealing Temperature on the Thermochromic Properties of VO2/TiO2 Thin Film[J]. IRON STEEL VANADIUM TITANIUM, 2015, 36(3): 35-40. doi: 10.7513/j.issn.1004-7638.2015.03.008
Citation:
Zhang Yubo, Miao Jingguo, Li Zhihong, Huang Wanxia. Effects of Interlayer Annealing Temperature on the Thermochromic Properties of VO2/TiO2 Thin Film[J]. IRON STEEL VANADIUM TITANIUM, 2015, 36(3): 35-40. doi: 10.7513/j.issn.1004-7638.2015.03.008
Zhang Yubo, Miao Jingguo, Li Zhihong, Huang Wanxia. Effects of Interlayer Annealing Temperature on the Thermochromic Properties of VO2/TiO2 Thin Film[J]. IRON STEEL VANADIUM TITANIUM, 2015, 36(3): 35-40. doi: 10.7513/j.issn.1004-7638.2015.03.008
Citation:
Zhang Yubo, Miao Jingguo, Li Zhihong, Huang Wanxia. Effects of Interlayer Annealing Temperature on the Thermochromic Properties of VO2/TiO2 Thin Film[J]. IRON STEEL VANADIUM TITANIUM, 2015, 36(3): 35-40. doi: 10.7513/j.issn.1004-7638.2015.03.008
TiO2 interlayer was deposited on the mica substrate,and the VO2 film was fabricated on the TiO2 interlayer under UV light irradiated. Video-based contact angle measuring device was used to analyze the hydrophilicity of the TiO2 interlayer. XRD,FTIR and UV-vis were used to analyze the microstructure and the thermochromic properties of the VO2/ TiO2 composite films. The results suggest that the hydrophilicity of the TiO2 film can be enhanced under ultraviolet excitation,and it is beneficial to coat V sol film uniformly on the TiO2/ mica substrate. The VO2/ TiO2 composite films grow in a preferred orientation along the (011) direction under 510 ~ 560 ℃ of TiO2 interlayer heat treating temperature. The transition temperature and hysteresis width of the composite films are reduced. The composite films grow in a preferred orientation along the (111) direction under 460 ℃ of annealing temperature for the TiO2 interlayer,with more than 92% of shielding efficiency.