Zeng Jianhua, Chen Yong, Wang Xinhua, Jiang Min, Yang Senxiang, Zhang Min, Pan Hong. Study on Refining Technology of High Quality Cord Steel Production[J]. IRON STEEL VANADIUM TITANIUM, 2015, 36(6): 94-100. doi: 10.7513/j.issn.1004-7638.2015.06.018
Citation:
Zeng Jianhua, Chen Yong, Wang Xinhua, Jiang Min, Yang Senxiang, Zhang Min, Pan Hong. Study on Refining Technology of High Quality Cord Steel Production[J]. IRON STEEL VANADIUM TITANIUM, 2015, 36(6): 94-100. doi: 10.7513/j.issn.1004-7638.2015.06.018
Zeng Jianhua, Chen Yong, Wang Xinhua, Jiang Min, Yang Senxiang, Zhang Min, Pan Hong. Study on Refining Technology of High Quality Cord Steel Production[J]. IRON STEEL VANADIUM TITANIUM, 2015, 36(6): 94-100. doi: 10.7513/j.issn.1004-7638.2015.06.018
Citation:
Zeng Jianhua, Chen Yong, Wang Xinhua, Jiang Min, Yang Senxiang, Zhang Min, Pan Hong. Study on Refining Technology of High Quality Cord Steel Production[J]. IRON STEEL VANADIUM TITANIUM, 2015, 36(6): 94-100. doi: 10.7513/j.issn.1004-7638.2015.06.018
1. Pangang Group Research Institute Co., Ltd., State Key Laboratory of Vanadium and Titanium Resources Comprehensive Utilization, Panzhihua 617000, Sichuan, China;
2. University of Science and Technology Beijing, Beijing 100083, China;
3. Pangang Group Panzhihua Steel and Vanadium Co., Ltd., Panzhihua 617062, Sichuan, China
In order to meet the strict requirements of inclusion and cleanliness for high quality cord steel,top slag composition and refining process had been studied through predication and industrial practice.The results show that the inclusions can meet the requirements of plasticity at lower melting temperature when the tap slag basicity (CaO/SiO2) and Al2O3 content are controlled at about 1.0 and in the range of 6%~8%,respectively. Compared with the process of DeS-LD-LF-Ar-CC,the process of DeS-LD-LFRH-CC can lead to inclusion meeting requirements of plasticity and further reducing content of T[O] and [N],and thus improve the cleanliness. The average wire broken ratio of cord steel products is 0.47 time per ton and the fatigue lifetimes reached over 20,000 cycles.