Jin Juan, Wu Run, Tang Mengxia, Fan Lixia, Zhou Herong. Effect of Annealing Processes on Microstructure and Recrystallization Texture of a Cold-rolled High Strength IF Steel[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(1): 148-152,162. doi: 10.7513/j.issn.1004-7638.2017.01.026
Citation:
Jin Juan, Wu Run, Tang Mengxia, Fan Lixia, Zhou Herong. Effect of Annealing Processes on Microstructure and Recrystallization Texture of a Cold-rolled High Strength IF Steel[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(1): 148-152,162. doi: 10.7513/j.issn.1004-7638.2017.01.026
Jin Juan, Wu Run, Tang Mengxia, Fan Lixia, Zhou Herong. Effect of Annealing Processes on Microstructure and Recrystallization Texture of a Cold-rolled High Strength IF Steel[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(1): 148-152,162. doi: 10.7513/j.issn.1004-7638.2017.01.026
Citation:
Jin Juan, Wu Run, Tang Mengxia, Fan Lixia, Zhou Herong. Effect of Annealing Processes on Microstructure and Recrystallization Texture of a Cold-rolled High Strength IF Steel[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(1): 148-152,162. doi: 10.7513/j.issn.1004-7638.2017.01.026
1. Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China;
2. Iron and Steel Group Corporation, Panzhihua 617000, Sichuan, China
A cold-rolled high strength IF steel was annealed at two different heating rate to study the evolution of microstructure and recrystallization texture of IF steels. The results show that the γ-fier({111} or(ND‖<111>)) of IF steel form at both of two recrystallization annealing processes.When the samples are heated at fast rate of 350 ℃/min,the recrystallization grains grow from the merging of subgrains and show equiaxed morphology.The orientation of recrystallization grains was consistent with the surrounding deformation matrix.When the samples are heated at slow rate of 2 ℃/min,the new grains grow from grain boundary bowing,showing pancake grains along the rolling direction with weak orientation to the deformed grains.The density of γ-{111} orientation of the samples with slow heating rate are stronger than that with fast heating rate.The results are of great significance to improve the deep drawability of the thin sheet.