Chen Pengfei, Ai Liqun, Li Qiang, Li Yaqiang, Liu Xinliang. Experimental study of Gas-solid Decarburization process of 1.5 mm Fe-C Alloy Ribbon[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(4): 155-159. doi: 10.7513/j.issn.1004-7638.2017.04.027
Citation:
Chen Pengfei, Ai Liqun, Li Qiang, Li Yaqiang, Liu Xinliang. Experimental study of Gas-solid Decarburization process of 1.5 mm Fe-C Alloy Ribbon[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(4): 155-159. doi: 10.7513/j.issn.1004-7638.2017.04.027
Chen Pengfei, Ai Liqun, Li Qiang, Li Yaqiang, Liu Xinliang. Experimental study of Gas-solid Decarburization process of 1.5 mm Fe-C Alloy Ribbon[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(4): 155-159. doi: 10.7513/j.issn.1004-7638.2017.04.027
Citation:
Chen Pengfei, Ai Liqun, Li Qiang, Li Yaqiang, Liu Xinliang. Experimental study of Gas-solid Decarburization process of 1.5 mm Fe-C Alloy Ribbon[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(4): 155-159. doi: 10.7513/j.issn.1004-7638.2017.04.027
In order to investigate the decarburization law of 1.5 mm thick iron-carbon alloy strip,an iron carbon steel strip with initial carbon mass fraction of 3.2% was used and placed into a decarburization furnace under weak oxidizing atmosphere created by Ar-H2-H2O mixed gas and heated. The samples were heated to 1 293 K,1 353 K and 1 413 K with holding time of 10~50 minutes respectively for the decarburization treatment via gas-solid reaction.the sample.The results show that the decarburization reaction is a approximate first-order reaction,and the activation energy is 111.9 kJ/mol.The decarburization temperature has a significant effect on the decarburization effect.The final carbon content as function of holding time can be expressed as wt=3.2e((0.196 12-1.62×10-4T)t.