Wang Xiru, Zhang Xuefeng, Chen Min. Research Progress on Microstructure and Mechanical Properties of(Ti,M)(C,N)-based Cermets[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(6): 37-42. doi: 10.7513/j.issn.1004-7638.2017.06.007
Citation:
Wang Xiru, Zhang Xuefeng, Chen Min. Research Progress on Microstructure and Mechanical Properties of(Ti,M)(C,N)-based Cermets[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(6): 37-42. doi: 10.7513/j.issn.1004-7638.2017.06.007
Wang Xiru, Zhang Xuefeng, Chen Min. Research Progress on Microstructure and Mechanical Properties of(Ti,M)(C,N)-based Cermets[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(6): 37-42. doi: 10.7513/j.issn.1004-7638.2017.06.007
Citation:
Wang Xiru, Zhang Xuefeng, Chen Min. Research Progress on Microstructure and Mechanical Properties of(Ti,M)(C,N)-based Cermets[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(6): 37-42. doi: 10.7513/j.issn.1004-7638.2017.06.007
(Ti,M)(C,N)-based cermets are important tools and coating materials.The domestic and abroad research progress of microstructure and mechanical properties of (Ti,M)(C,N)-based cermets was reviewed,and the characteristics of black core-white inner ring-gray outer ring and white core-grey ring microstructure in(Ti,M) (C,N)-based cermets were elaborated. The effects of TiC/TiN content,Co,Ni binder phase content,Mo,WC,VC,Cr3C2,TaC and NbC additives on the microstructure and mechanical properties of(Ti,M)(C,N)-based cermets were introduced. The next research directions was also pointed out.