Gao Yang, Gui Yongliang, Song Chunyan, Hu Binsheng, Wang Yawen. Effect of Nucleating Agent on Crystallization Behavior and Kinetics of Blast Furnace Slag Glass Ceramics[J]. IRON STEEL VANADIUM TITANIUM, 2018, 39(1): 72-77. doi: 10.7513/j.issn.1004-7638.2018.01.014
Citation:
Gao Yang, Gui Yongliang, Song Chunyan, Hu Binsheng, Wang Yawen. Effect of Nucleating Agent on Crystallization Behavior and Kinetics of Blast Furnace Slag Glass Ceramics[J]. IRON STEEL VANADIUM TITANIUM, 2018, 39(1): 72-77. doi: 10.7513/j.issn.1004-7638.2018.01.014
Gao Yang, Gui Yongliang, Song Chunyan, Hu Binsheng, Wang Yawen. Effect of Nucleating Agent on Crystallization Behavior and Kinetics of Blast Furnace Slag Glass Ceramics[J]. IRON STEEL VANADIUM TITANIUM, 2018, 39(1): 72-77. doi: 10.7513/j.issn.1004-7638.2018.01.014
Citation:
Gao Yang, Gui Yongliang, Song Chunyan, Hu Binsheng, Wang Yawen. Effect of Nucleating Agent on Crystallization Behavior and Kinetics of Blast Furnace Slag Glass Ceramics[J]. IRON STEEL VANADIUM TITANIUM, 2018, 39(1): 72-77. doi: 10.7513/j.issn.1004-7638.2018.01.014
Taken Tangshan iron and steel blast furnace slag as the main raw material,Cr2O3,TiO2,Fe2O3 and P2O5 nucleating agent had been added with a certain proportion of other raw materials,and the blast furnace slag microcrystalline glass had been prepared by melting method. Differential thermal analyzer(SEM) and electron scanning microscope(SEM) were used to investigate the effect of nucleating agents on the crystallization behavior of glass ceramics. The results show that 2% Cr2O3 and 8% P2O5 can form microcrystalline glass with fine grain and uniform distribution. Addition of 8% TiO2 and 6% Fe2O3 can not result in an ideal microcrystalline glass.