Guo Chen, Zhang Wei, Wang Hui, Xing Hongwei. Effect of Gas Quenching Behavior of Modified Steel Slag on Digestion of f-CaO[J]. IRON STEEL VANADIUM TITANIUM, 2019, 40(5): 71-77. doi: 10.7513/j.issn.1004-7638.2019.05.013
Citation:
Guo Chen, Zhang Wei, Wang Hui, Xing Hongwei. Effect of Gas Quenching Behavior of Modified Steel Slag on Digestion of f-CaO[J]. IRON STEEL VANADIUM TITANIUM, 2019, 40(5): 71-77. doi: 10.7513/j.issn.1004-7638.2019.05.013
Guo Chen, Zhang Wei, Wang Hui, Xing Hongwei. Effect of Gas Quenching Behavior of Modified Steel Slag on Digestion of f-CaO[J]. IRON STEEL VANADIUM TITANIUM, 2019, 40(5): 71-77. doi: 10.7513/j.issn.1004-7638.2019.05.013
Citation:
Guo Chen, Zhang Wei, Wang Hui, Xing Hongwei. Effect of Gas Quenching Behavior of Modified Steel Slag on Digestion of f-CaO[J]. IRON STEEL VANADIUM TITANIUM, 2019, 40(5): 71-77. doi: 10.7513/j.issn.1004-7638.2019.05.013
School of Metallurgy and Energy, North China University of Technology, Key Laboratory of Ministry of Modern Metallurgical Technology, Tangshan 063009, Hebei, China
In this paper blast furnace slag with different content(0%,15%,25%,35%) was selected to carry out quenching and tempering reconstruction on steel slag,and then high-temperature gas quenching had been performed.Influence of gas quenching behavior on the elimination of f-CaO by reconstructed slag had been investigated.The results show that gas quenching is beneficial to the digestion of f-CaO in steel slag.The smaller particle size of steel slag can achieve better the digestion efficiency.XRD and mineral phase analysis show that after gas quenching the mineral phase composition of steel slag is composed of glass phase,RO phase,dicalcium silicate,periclase and so on.