Lin Wenkang, Hu Peng. Influence of TiO2 Content and Basicity Level on the Metallogenic Regularity of V-Ti Sinter[J]. IRON STEEL VANADIUM TITANIUM, 2020, 41(2): 94-100. doi: 10.7513/j.issn.1004-7638.2020.02.018
Citation:
Lin Wenkang, Hu Peng. Influence of TiO2 Content and Basicity Level on the Metallogenic Regularity of V-Ti Sinter[J]. IRON STEEL VANADIUM TITANIUM, 2020, 41(2): 94-100. doi: 10.7513/j.issn.1004-7638.2020.02.018
Lin Wenkang, Hu Peng. Influence of TiO2 Content and Basicity Level on the Metallogenic Regularity of V-Ti Sinter[J]. IRON STEEL VANADIUM TITANIUM, 2020, 41(2): 94-100. doi: 10.7513/j.issn.1004-7638.2020.02.018
Citation:
Lin Wenkang, Hu Peng. Influence of TiO2 Content and Basicity Level on the Metallogenic Regularity of V-Ti Sinter[J]. IRON STEEL VANADIUM TITANIUM, 2020, 41(2): 94-100. doi: 10.7513/j.issn.1004-7638.2020.02.018
In order to investigate the influence of different TiO2 content and basicity level on the technical and economic indexes of V-Ti sintering and the metallurgical properties of V-Ti sinter,so as to determine a better sintering and blast furnace material mixture,an experimental study was carried out to reduce the TiO2 content of sinter and increase the basicity level of sinter.Experimental results show that with the decrease of TiO2 content and the increase of basicity of V-Ti sinter,the technical indexes of sinter are improved significantly.When the content of TiO2 in sinter decreases from 6.0% to 0.5% and the basicity level is increased from 2.0 to 2.5,the yield is increased by 5.21%,the drum strength is increased by 5.60%,and the utilization coefficient is increased by more than 25% compared with those of the reference period.