JIANG Chang-lin, ZHU Tao, PAN Guo-ping. DISCUSSION ON PRODUCTION OF VANADIUM-MICROALLOYING STEEL IN CSP LINE[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(1): 39-43.
Citation:
JIANG Chang-lin, ZHU Tao, PAN Guo-ping. DISCUSSION ON PRODUCTION OF VANADIUM-MICROALLOYING STEEL IN CSP LINE[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(1): 39-43.
JIANG Chang-lin, ZHU Tao, PAN Guo-ping. DISCUSSION ON PRODUCTION OF VANADIUM-MICROALLOYING STEEL IN CSP LINE[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(1): 39-43.
Citation:
JIANG Chang-lin, ZHU Tao, PAN Guo-ping. DISCUSSION ON PRODUCTION OF VANADIUM-MICROALLOYING STEEL IN CSP LINE[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(1): 39-43.
The strengthening and toughing mechanism of vanadium-microalloying steel and the technological trait of CSP line are reviewed.The feasibility of applying vanadium-microalloying in CSP line and some noticeable problems are discussed.The technological trait of controlled rolling and accelerated cooling for vanadium-microalloying steel is the integration of RCR and AC,and it is regarded as the characteristic and advantage of CSP line.