SU Liang, TIAN Naiyuan, MAO Xinping, LIN Zhenyuan. Influence of Liquid Core Reduction on Mechanical Properties of High Strength Weathering Steels in Thin Slab Casting and Direct Rolling Process[J]. IRON STEEL VANADIUM TITANIUM, 2008, 29(2): 14-17.
Citation:
SU Liang, TIAN Naiyuan, MAO Xinping, LIN Zhenyuan. Influence of Liquid Core Reduction on Mechanical Properties of High Strength Weathering Steels in Thin Slab Casting and Direct Rolling Process[J]. IRON STEEL VANADIUM TITANIUM, 2008, 29(2): 14-17.
SU Liang, TIAN Naiyuan, MAO Xinping, LIN Zhenyuan. Influence of Liquid Core Reduction on Mechanical Properties of High Strength Weathering Steels in Thin Slab Casting and Direct Rolling Process[J]. IRON STEEL VANADIUM TITANIUM, 2008, 29(2): 14-17.
Citation:
SU Liang, TIAN Naiyuan, MAO Xinping, LIN Zhenyuan. Influence of Liquid Core Reduction on Mechanical Properties of High Strength Weathering Steels in Thin Slab Casting and Direct Rolling Process[J]. IRON STEEL VANADIUM TITANIUM, 2008, 29(2): 14-17.
Ti-microalloyed High Strength Weathering Steel was first produced by CSP process at Zhujiang Steel Co.,Ltd.,Effects of two different processes(with LCR or without LCR) on the mechanical properties and microstructure of the slab and strip were discussed.The results showed that all strips were of very fine microstructure and excellent mechanical property,but mechanical properties of slab by LCR are more homegeneous,properties of strip are slightly better contrast with one of without LCR.And thickness of continuous casting slab just fit with direct rolling.