In accordance with the coexistence theory of slag structure and phase diagram,the Calculating models of mass action concentration for the FeO-TiO2,FeO-Fe2O3-TiO2 slag systems have been deduced,The agreement between the calculated oxidizability and measured results is satisfactory. It is shown that the coexistence theory of slag structure is applicable to the above mentioned slag systems.