THE BEHAVIOR OF Ti REDUCTION IN SMELTING REDUCTION SLAG OF THE SYSTEM CaO-Sio2-Al2O3-MgO-TiO2

Feng Keqin; Zhang Binghuai

Dec. 1994

Article Contents

Article Navigation > IRON STEEL VANADIUM TITANIUM > 1994 > 15(4): 32-37,49

Feng Keqin, Zhang Binghuai. THE BEHAVIOR OF Ti REDUCTION IN SMELTING REDUCTION SLAG OF THE SYSTEM CaO-Sio2-Al2O3-MgO-TiO2[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(4): 32-37,49.

Citation:

Feng Keqin, Zhang Binghuai. THE BEHAVIOR OF Ti REDUCTION IN SMELTING REDUCTION SLAG OF THE SYSTEM CaO-Sio₂-Al₂O₃-MgO-TiO₂[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(4): 32-37,49.

Feng Keqin, Zhang Binghuai. THE BEHAVIOR OF Ti REDUCTION IN SMELTING REDUCTION SLAG OF THE SYSTEM CaO-Sio2-Al2O3-MgO-TiO2[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(4): 32-37,49.

Citation:

Feng Keqin, Zhang Binghuai. THE BEHAVIOR OF Ti REDUCTION IN SMELTING REDUCTION SLAG OF THE SYSTEM CaO-Sio₂-Al₂O₃-MgO-TiO₂[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(4): 32-37,49.

PDF( 241 KB)

THE BEHAVIOR OF Ti REDUCTION IN SMELTING REDUCTION SLAG OF THE SYSTEM CaO-Sio₂-Al₂O₃-MgO-TiO₂

Feng Keqin¹,
Zhang Binghuai²

1. Sichuan Union University;
2. Chongqing University

Available Online: 2023-12-07

Abstract

Abstract

Experiments have been conducted to study the behavior of titanium reduction between the CaO-SiO₂-Al₂O₃-MgO-TiO₂ slag and carbon saturated iron melts in the smelting reduction process. The influences of TiO₂-content in the slag,slag basicity(CaO/SiO₂),reduction temperature and quantity of iron bath on the titanium reduction have also been investigated.
- smelting reduction,
- iron bath,
- titanium reduction