Liu Bianmei, Xiong Renjin, Jiang Dongmei, Zhang Huaifa, Yang Weizhong, Zhou Dali. Study on Preparing W-doped Vanadium Dioxide Film by Inorganic Sol-gel Process[J]. IRON STEEL VANADIUM TITANIUM, 2007, 28(3): 33-36.
Citation:
Liu Bianmei, Xiong Renjin, Jiang Dongmei, Zhang Huaifa, Yang Weizhong, Zhou Dali. Study on Preparing W-doped Vanadium Dioxide Film by Inorganic Sol-gel Process[J]. IRON STEEL VANADIUM TITANIUM, 2007, 28(3): 33-36.
Liu Bianmei, Xiong Renjin, Jiang Dongmei, Zhang Huaifa, Yang Weizhong, Zhou Dali. Study on Preparing W-doped Vanadium Dioxide Film by Inorganic Sol-gel Process[J]. IRON STEEL VANADIUM TITANIUM, 2007, 28(3): 33-36.
Citation:
Liu Bianmei, Xiong Renjin, Jiang Dongmei, Zhang Huaifa, Yang Weizhong, Zhou Dali. Study on Preparing W-doped Vanadium Dioxide Film by Inorganic Sol-gel Process[J]. IRON STEEL VANADIUM TITANIUM, 2007, 28(3): 33-36.
W-doped vanadium dioxide film was prepared by dipping V-W commixed sol on surface of glass slide and reducing in hydrogen atmosphere. XRD and XPS were used to analyze the phase components of the film. Synthetic conditions of steady V-W commixed sol and W-doped VO2 film were researched.Results show that the phase transition temperature (Tc) of W-doped Vanadium dioxide film prepared by an inorganic sol-gel process can be reduced to room temperature. At the nearby of phase transition temperature, the resistance and the IR transmission of W-doped vanadium dioxide film have a notable change, and the visible light transmission decreases with the rising of environment temperature.