Huang Shouhua, Zhang Ronglu, Pan Jingye. PILOT TEST OF CARBONIZATION OF THE MOLTEN BLAST FURNACE TiO2 SLAG AT PANZHIHUA IRON AND STEEL COMPANY[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(2): 17-21.
Citation:
Huang Shouhua, Zhang Ronglu, Pan Jingye. PILOT TEST OF CARBONIZATION OF THE MOLTEN BLAST FURNACE TiO2 SLAG AT PANZHIHUA IRON AND STEEL COMPANY[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(2): 17-21.
Huang Shouhua, Zhang Ronglu, Pan Jingye. PILOT TEST OF CARBONIZATION OF THE MOLTEN BLAST FURNACE TiO2 SLAG AT PANZHIHUA IRON AND STEEL COMPANY[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(2): 17-21.
Citation:
Huang Shouhua, Zhang Ronglu, Pan Jingye. PILOT TEST OF CARBONIZATION OF THE MOLTEN BLAST FURNACE TiO2 SLAG AT PANZHIHUA IRON AND STEEL COMPANY[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(2): 17-21.
The paper describes the pilot test of carbonization of the molten blast furnace TiO2 slag in a 2250kVA electric furnace,The process of carbonization of molten TiO2 slag has a tendancy for better materials mixing with larger electric furnace. During carbonization physical heat of the molten slag can be used resulting in 40% reduction of power consumption and 30% increase of productivity.The wider range of temperature has made the operation much easier.