The new Ⅲ-grade 20MnSiV concrete steel was smelted in converter with vanadium bearing ball,i.e. the mixture composed of vanadium bearing slag and reductant.The results obtained show that while low-alloy steel is made, it is feasible and economic to replace ferrovanadium or V2O5 alloying with vanadium bearing ball alloying in molten steel ladle.