Zhen Yulan, Zhang Guohua, Zhou Guozhi. Recovery of Ti from Titanium-bearing Blast Furnace Slag by Aluminum[J]. IRON STEEL VANADIUM TITANIUM, 2014, 35(5): 40-44. doi: 10.7513/j.issn.1004-7638.2014.05.009
Citation:
Zhen Yulan, Zhang Guohua, Zhou Guozhi. Recovery of Ti from Titanium-bearing Blast Furnace Slag by Aluminum[J]. IRON STEEL VANADIUM TITANIUM, 2014, 35(5): 40-44. doi: 10.7513/j.issn.1004-7638.2014.05.009
Zhen Yulan, Zhang Guohua, Zhou Guozhi. Recovery of Ti from Titanium-bearing Blast Furnace Slag by Aluminum[J]. IRON STEEL VANADIUM TITANIUM, 2014, 35(5): 40-44. doi: 10.7513/j.issn.1004-7638.2014.05.009
Citation:
Zhen Yulan, Zhang Guohua, Zhou Guozhi. Recovery of Ti from Titanium-bearing Blast Furnace Slag by Aluminum[J]. IRON STEEL VANADIUM TITANIUM, 2014, 35(5): 40-44. doi: 10.7513/j.issn.1004-7638.2014.05.009
School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, State Key Laboratory of Advanced Metallurgy, Beijing 100083, China
The recovery of Ti from titanium slag by alu minum was investigated.After smelting,Ti-Si-Al alloy and slag with high content of alumina were obtained.It is indicated from the experimental results that the recovery of Ti from titanium-bearing blast furnace slag by aluminum is technically feasible.The effective enrichment and separation can be achieved in a short time.The main factors affecting the smelting results are temperature,time,contents of reducing agent aluminum and flux CaO.The effective enrichment and separation can be achieved with wslag:wAl=100:25.98 at 1 600℃ for 10 min.At the same time,adding CaO is helpful to achieve the separation of the alloy and slag.