Liu Weidong, Lin Cuiqing. Vanadium-titanium Composite Infiltration Process on the Surface of Cold Working Die Steel[J]. IRON STEEL VANADIUM TITANIUM, 2016, 37(1): 61-64. doi: 10.7513/j.issn.1004-7638.2016.01.013
Citation:
Liu Weidong, Lin Cuiqing. Vanadium-titanium Composite Infiltration Process on the Surface of Cold Working Die Steel[J]. IRON STEEL VANADIUM TITANIUM, 2016, 37(1): 61-64. doi: 10.7513/j.issn.1004-7638.2016.01.013
Liu Weidong, Lin Cuiqing. Vanadium-titanium Composite Infiltration Process on the Surface of Cold Working Die Steel[J]. IRON STEEL VANADIUM TITANIUM, 2016, 37(1): 61-64. doi: 10.7513/j.issn.1004-7638.2016.01.013
Citation:
Liu Weidong, Lin Cuiqing. Vanadium-titanium Composite Infiltration Process on the Surface of Cold Working Die Steel[J]. IRON STEEL VANADIUM TITANIUM, 2016, 37(1): 61-64. doi: 10.7513/j.issn.1004-7638.2016.01.013
Vanadium-titanium composite infiltration coating was produced on the surface of Cr12MoV cold working die steel for different time respectively with V2O5 and TiO2 as vanadium and titanium donor,and the microstructure,phase structure,corrosion and wear resistance were tested and analyzed.The results show that vanadium-titanium composite infiltration coating can be successfully produced on the surface of Cr12MoV cold working die steel at 890℃,and the composite infiltration coating is composed of VC、TiC and a spot of V8C7.To improve the corrosion resistance and wear resistance of cold working die steel,the composite infiltrating time was optimized at 7 h.