Long Yue, Du Peipei, Zhang Liangjin, Li Zhihui, Zhang Yuzhu. The Physical and Chemical Properties of Slag Wool by Direct Fibration of Blast Furnace Slag[J]. IRON STEEL VANADIUM TITANIUM, 2016, 37(2): 78-83. doi: 10.7513/j.issn.1004-7638.2016.02.014
Citation:
Long Yue, Du Peipei, Zhang Liangjin, Li Zhihui, Zhang Yuzhu. The Physical and Chemical Properties of Slag Wool by Direct Fibration of Blast Furnace Slag[J]. IRON STEEL VANADIUM TITANIUM, 2016, 37(2): 78-83. doi: 10.7513/j.issn.1004-7638.2016.02.014
Long Yue, Du Peipei, Zhang Liangjin, Li Zhihui, Zhang Yuzhu. The Physical and Chemical Properties of Slag Wool by Direct Fibration of Blast Furnace Slag[J]. IRON STEEL VANADIUM TITANIUM, 2016, 37(2): 78-83. doi: 10.7513/j.issn.1004-7638.2016.02.014
Citation:
Long Yue, Du Peipei, Zhang Liangjin, Li Zhihui, Zhang Yuzhu. The Physical and Chemical Properties of Slag Wool by Direct Fibration of Blast Furnace Slag[J]. IRON STEEL VANADIUM TITANIUM, 2016, 37(2): 78-83. doi: 10.7513/j.issn.1004-7638.2016.02.014
1. School of Metallurgy and Energy Resource, North China University of Science and Technology, Modern Metallurgical Technique Key Laboratory of Ministry of Education, Tangshan 063009, Hebei, China;
2. School of Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China
Slag wool was prepared in laboratory by four-roller centrifugation method using blast furnace slag with 1.25 of acidity coefficient as raw material.The microstructure,diameter,shot content and moisture,mineragraphy and crystallization temperature of the obtained slag wool were analyzed.The results show that the slag wool is solid cylindrical fiber with smooth surface,and its diameter,shot content and moisture is respectively 4.9 μm,3.76% and 0.73%,satisfying the international standard overall.Furthermore,the slag wool has a higher vitrification degree with about 882℃ of crystallization temperature and almost no crystallization except for a very small amount of calcium aluminum melilite(Ca[Al(AlSi)O7]) and calcium magnesium melilite(Ca2MgSi2O7).