Xing Hongwei, Gu Shaopeng, Liu Xiaofan, Fu Junkai. Preparation of Composite TiO2 Loaded on Blast Furnace Slag Fibre by Impregnation and Depositing Method[J]. IRON STEEL VANADIUM TITANIUM, 2016, 37(4): 83-88. doi: 10.7513/j.issn.1004-7638.2016.04.016
Citation:
Xing Hongwei, Gu Shaopeng, Liu Xiaofan, Fu Junkai. Preparation of Composite TiO2 Loaded on Blast Furnace Slag Fibre by Impregnation and Depositing Method[J]. IRON STEEL VANADIUM TITANIUM, 2016, 37(4): 83-88. doi: 10.7513/j.issn.1004-7638.2016.04.016
Xing Hongwei, Gu Shaopeng, Liu Xiaofan, Fu Junkai. Preparation of Composite TiO2 Loaded on Blast Furnace Slag Fibre by Impregnation and Depositing Method[J]. IRON STEEL VANADIUM TITANIUM, 2016, 37(4): 83-88. doi: 10.7513/j.issn.1004-7638.2016.04.016
Citation:
Xing Hongwei, Gu Shaopeng, Liu Xiaofan, Fu Junkai. Preparation of Composite TiO2 Loaded on Blast Furnace Slag Fibre by Impregnation and Depositing Method[J]. IRON STEEL VANADIUM TITANIUM, 2016, 37(4): 83-88. doi: 10.7513/j.issn.1004-7638.2016.04.016
School of Metallurgy and Energy, North China University of Science and Technology, Key Laboratory of Modern Metallurgy Technology of Hebei Province, Key Laboratory of Inorganic Nonmetallic Materials of Hebei Province, Tangshan 063009, Hebei, China
Received Date: 2016-01-20 Available Online:
2023-12-04
Composite material(TiO2/BFSF) of TiO2 loaded on blast furnace slag fibre(BFSF) was prepared by impregnation-depositing process using BFSF as the carrier. The crystal form,grain size,specific surface area of TiO2 and microstructure of the composite TiO2/BFSF were characterized by XRD,particle size analyzer and Zeta potential meter,N2 adsorption and desorption instrument,SEM and EDS,respectively.The photocatalysis performances of TiO2/BFSF were evaluated by degradation of methylene blue(MB) simulating dyeing waste water. The results show that with 3 times of impregnation-depositing in 20 g/L TiO2 suspension system,TiO2 can be uniformly coated on the BFSF and 94.8% MB can be degraded by composite TiO2/BFSF under the ultraviolet light irradiation for 180 min.After 4 times of recycle the degradation rate of MB is still maintained at 65%.