Tang Hongjian, Zhang Li, Sun Zhaohui, Chen Haijun, Yu Bin, Du Guangchao. Study on Preparation of High-purity V2O5 by Solvent Extraction from Acid Leaching Vanadium-containing Solution[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(1): 15-21. doi: 10.7513/j.issn.1004-7638.2017.01.003
Citation:
Tang Hongjian, Zhang Li, Sun Zhaohui, Chen Haijun, Yu Bin, Du Guangchao. Study on Preparation of High-purity V2O5 by Solvent Extraction from Acid Leaching Vanadium-containing Solution[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(1): 15-21. doi: 10.7513/j.issn.1004-7638.2017.01.003
Tang Hongjian, Zhang Li, Sun Zhaohui, Chen Haijun, Yu Bin, Du Guangchao. Study on Preparation of High-purity V2O5 by Solvent Extraction from Acid Leaching Vanadium-containing Solution[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(1): 15-21. doi: 10.7513/j.issn.1004-7638.2017.01.003
Citation:
Tang Hongjian, Zhang Li, Sun Zhaohui, Chen Haijun, Yu Bin, Du Guangchao. Study on Preparation of High-purity V2O5 by Solvent Extraction from Acid Leaching Vanadium-containing Solution[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(1): 15-21. doi: 10.7513/j.issn.1004-7638.2017.01.003
1. Pangang Group Research Institute Co., Ltd., State Key Laboratory of Vanadium and Titanium Resources Comprehensive Utilization, Panzhihua 617000, Sichuan, China;
2. School of Materials & Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China
According to characteristics of low vanadium concentration and multitudinous impurities for the sulphuric acid leaching solution of vanadium slag roasted with calcium components,high-purity vanadium pentoxide (V2O5) was prepared by solvent extraction from the acid leaching vanadium-containing solution. The processes of extraction,washing,stripping and acidic precipitation of vanadium by ammonium salt were systematically researched in order to explore a completely clean and efficient method for extracting vanadium from acid leaching vanadium-containing solution and provide data support for the development and application of high-purity V2O5 preparation technology. The results show that V2O5 with 99.991 5% of purity can be obtained and the recovery rate of vanadium for the whole process is up to 88.78% under the optimal conditions.