Wang Xingjuan, Fan Yapeng, Zhu Liguang, Wang Lijie, Wu Binbin, Tian Kuo. Influence of CaF2 Content in the Continuous Casting Mold Flux on the Devitrification Properties[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(1): 106-112. doi: 10.7513/j.issn.1004-7638.2017.01.019
Citation:
Wang Xingjuan, Fan Yapeng, Zhu Liguang, Wang Lijie, Wu Binbin, Tian Kuo. Influence of CaF2 Content in the Continuous Casting Mold Flux on the Devitrification Properties[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(1): 106-112. doi: 10.7513/j.issn.1004-7638.2017.01.019
Wang Xingjuan, Fan Yapeng, Zhu Liguang, Wang Lijie, Wu Binbin, Tian Kuo. Influence of CaF2 Content in the Continuous Casting Mold Flux on the Devitrification Properties[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(1): 106-112. doi: 10.7513/j.issn.1004-7638.2017.01.019
Citation:
Wang Xingjuan, Fan Yapeng, Zhu Liguang, Wang Lijie, Wu Binbin, Tian Kuo. Influence of CaF2 Content in the Continuous Casting Mold Flux on the Devitrification Properties[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(1): 106-112. doi: 10.7513/j.issn.1004-7638.2017.01.019
1. College of Metallurgy & Energy, Key Laboratory for Advanced Metallurgy Technology, Hebei Province High Quality Steel Continuous Casting Engineering Technology Research Center, North China University of Science and Technology, Tangshan 063009, Hebei, China;
2. Tangshan Iron and Steel Company, Hebei Iron and Steel Group, Tangshan 063016, Hebei, China
TTT curve was constructed using SHTT II melting and crystallization temperature measuring instrument,then the mold flux devitrification activation energy was calculated at different levels of CaF2.To calculate the rate of crystallization and analysis crystalline phase,X-ray diddractometer combining with the JADE software are utilized.Various surface morphology of slag film protection with different CaF2 content under the different temperature treatment was observed under the metallographic microscope,exploring the impact of CaF2 on the devitrification of slag.It is found out that the temperature and activation energy of initial devitrified phenomenon decreases and the roughness on the surface of flux film increases with the CaF2 content increasing.The mineral species tend to be single with treating temperature of glassy flux film increasing.