Wang Haibo, Chen Xinhong, Wu Xiaoping, Wang Bin, Luo Zhiqiang. Effect of Sand Milling Times on the Quality of TiO2 Initial Product[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(3): 34-37. doi: 10.7513/j.issn.1004-7638.2017.03.006
Citation:
Wang Haibo, Chen Xinhong, Wu Xiaoping, Wang Bin, Luo Zhiqiang. Effect of Sand Milling Times on the Quality of TiO2 Initial Product[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(3): 34-37. doi: 10.7513/j.issn.1004-7638.2017.03.006
Wang Haibo, Chen Xinhong, Wu Xiaoping, Wang Bin, Luo Zhiqiang. Effect of Sand Milling Times on the Quality of TiO2 Initial Product[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(3): 34-37. doi: 10.7513/j.issn.1004-7638.2017.03.006
Citation:
Wang Haibo, Chen Xinhong, Wu Xiaoping, Wang Bin, Luo Zhiqiang. Effect of Sand Milling Times on the Quality of TiO2 Initial Product[J]. IRON STEEL VANADIUM TITANIUM, 2017, 38(3): 34-37. doi: 10.7513/j.issn.1004-7638.2017.03.006
1. Pangang Group Research Institute Co., Ltd., State Key Laboratory of Vanadium and Titanium Resources Comprehensive Utilization, Panzhihua 617000, Sichuan, China;
2. Pangang Group Chongqing Titanium Industry Co., Ltd., Chongqing 400054, China
The influence of sand milling times on the quality of titanium dioxide (TiO2) initial product was investigated by horizontal sand mill,using roll milling TiO2 product as raw material and zirconia beads with different sizes as grinding media. The results show that with increase of sand milling times the pH and viscosity of the slurry are not changed substantially,particle size D50 decreases and the ratio of particles with size ≤1 μm increases gradually. Meanwhile,the length-diameter value of particles in the slurry decreases slowly with the degree of sphericity gradually improved,the quantity and size of the aggregates decreased,and the value of whiteness L and brightness for the obtained TiO2 increased step by step. TiO2 initial product with more uniform size distribution,higher value of whiteness and brightness can be obtained using 0.4mm zirconia beads,compared with those of the product prepared by 0.6 mm and 1.8 mm zirconia beads.