Liu Xinliang, Ai Liqun, Gao Jianxin, Li Yaqiang, Chen Pengfei, Li Qiang. Influence of Atmosphere Condition on Iron Sheet Gas-solid Decarburization Process[J]. IRON STEEL VANADIUM TITANIUM, 2018, 39(3): 86-93. doi: 10.7513/j.issn.1004-7638.2018.03.017
Citation:
Liu Xinliang, Ai Liqun, Gao Jianxin, Li Yaqiang, Chen Pengfei, Li Qiang. Influence of Atmosphere Condition on Iron Sheet Gas-solid Decarburization Process[J]. IRON STEEL VANADIUM TITANIUM, 2018, 39(3): 86-93. doi: 10.7513/j.issn.1004-7638.2018.03.017
Liu Xinliang, Ai Liqun, Gao Jianxin, Li Yaqiang, Chen Pengfei, Li Qiang. Influence of Atmosphere Condition on Iron Sheet Gas-solid Decarburization Process[J]. IRON STEEL VANADIUM TITANIUM, 2018, 39(3): 86-93. doi: 10.7513/j.issn.1004-7638.2018.03.017
Citation:
Liu Xinliang, Ai Liqun, Gao Jianxin, Li Yaqiang, Chen Pengfei, Li Qiang. Influence of Atmosphere Condition on Iron Sheet Gas-solid Decarburization Process[J]. IRON STEEL VANADIUM TITANIUM, 2018, 39(3): 86-93. doi: 10.7513/j.issn.1004-7638.2018.03.017
The study of gas-solid reactions is performed in order to investigate the impact of weak oxidizing atmosphere Ar-H2O-H2 on the 1 mm thick 4. 25% C iron-carbon alloy sheet. A serious of orthogonal experiments have been performed to investigate the influence of bath temperature,initial H2 content and gas flow on the decarburization of iron-carbon alloy ribbon.It is found out that the significance of gas flow,initial H2 content and bath temperature on decarburization sequentially decrease.When gas flow rate is in range of 200 ~500 mL·min-1,increasing flow rate can significantly improve the decarburization result.When water bath temperature exceeds 333 K,oxidation of iron takes place,and dense layer of Fe O appears when water bath temperature exceeds 343 K.Suitable parameters for the decarburization at 1 413 K are flowrate 500 mL·min-1,15% H2,bath temperature 333 K.