Xiong Xuegang, Zhang Kaihua, Wang Yi, Ye Xiaoyu. Influence of Vanadium Content on Austenite Recrystallization Rule of Low Carbon Steel[J]. IRON STEEL VANADIUM TITANIUM, 2019, 40(4): 121-125. doi: 10.7513/j.issn.1004-7638.2019.04.023
Citation:
Xiong Xuegang, Zhang Kaihua, Wang Yi, Ye Xiaoyu. Influence of Vanadium Content on Austenite Recrystallization Rule of Low Carbon Steel[J]. IRON STEEL VANADIUM TITANIUM, 2019, 40(4): 121-125. doi: 10.7513/j.issn.1004-7638.2019.04.023
Xiong Xuegang, Zhang Kaihua, Wang Yi, Ye Xiaoyu. Influence of Vanadium Content on Austenite Recrystallization Rule of Low Carbon Steel[J]. IRON STEEL VANADIUM TITANIUM, 2019, 40(4): 121-125. doi: 10.7513/j.issn.1004-7638.2019.04.023
Citation:
Xiong Xuegang, Zhang Kaihua, Wang Yi, Ye Xiaoyu. Influence of Vanadium Content on Austenite Recrystallization Rule of Low Carbon Steel[J]. IRON STEEL VANADIUM TITANIUM, 2019, 40(4): 121-125. doi: 10.7513/j.issn.1004-7638.2019.04.023
1. Pangang Group Research Institute Co., Ltd., State Key Laboratory of Vanadium and Titanium Resources Comprehensive Utilization, Panzhihua 617000, Sichuan, China;
2. Pangang Group Xichang Steel & Vanadium Co., Ltd., Xichang 615000, Sichuan, China
To investigate the dynamic recrystallization rule of vanadium microalloying low carbon steel and its influence factors,flow curves under dynamic recrystallization conditions of 4 kinds of V-N microalloy steels were obtined by experiments so that the relationship of peak stressσp,strain rateεandtemperature T was obtained from the flow curve.The effect of temperature and content of V,N on dynamic recrystallization model was studied.By the way,an Avrami model for V-N microalloy steels was establishedand and the dynamic recrystallization activation energy was obtained by regression.The results show that V has a limit effect on improving the dynamic recrystallization critical temperature,while V combined with N has the significant effect on the critical temperature so as to inhibit the dynamic recrystallization.