ZHU Tao, JIANG Chang-lin, HE Yi-zhu. TESTING ON PRODUCTION OF VANADIUM-MICROALLOYED HSLA STEEL WITH OVER 550 MPa STRENGTH IN CSP[J]. IRON STEEL VANADIUM TITANIUM, 2003, 24(4): 6-13.
Citation:
ZHU Tao, JIANG Chang-lin, HE Yi-zhu. TESTING ON PRODUCTION OF VANADIUM-MICROALLOYED HSLA STEEL WITH OVER 550 MPa STRENGTH IN CSP[J]. IRON STEEL VANADIUM TITANIUM, 2003, 24(4): 6-13.
ZHU Tao, JIANG Chang-lin, HE Yi-zhu. TESTING ON PRODUCTION OF VANADIUM-MICROALLOYED HSLA STEEL WITH OVER 550 MPa STRENGTH IN CSP[J]. IRON STEEL VANADIUM TITANIUM, 2003, 24(4): 6-13.
Citation:
ZHU Tao, JIANG Chang-lin, HE Yi-zhu. TESTING ON PRODUCTION OF VANADIUM-MICROALLOYED HSLA STEEL WITH OVER 550 MPa STRENGTH IN CSP[J]. IRON STEEL VANADIUM TITANIUM, 2003, 24(4): 6-13.
In order to produce HSLA steel which tensile strength exceeds 550 MPa on CSP line, chemical composition design, CSP continuous-casting simulation, rolling test and Gleeble experiment were carried out. The effect of vanadium-microalloying and controlled rolling & controlled cooling technique was investigated. The production process was drafted and this is the base for further investigating on vanadium-microalloying behavior on CSP line.