YU Chi-bin, YE Chuan-long, ZHAO Gang, ZHANG Yun-xiang, SONG Ping, SU Yi, CHEN Liang, CENG Ping. STUDY ON STATIC RECRYSTALLIZATION DEVELOPMENT AND MODEL IN HOT ROLLED Nb-Ti STEEL[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(1): 25-29.
Citation:
YU Chi-bin, YE Chuan-long, ZHAO Gang, ZHANG Yun-xiang, SONG Ping, SU Yi, CHEN Liang, CENG Ping. STUDY ON STATIC RECRYSTALLIZATION DEVELOPMENT AND MODEL IN HOT ROLLED Nb-Ti STEEL[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(1): 25-29.
YU Chi-bin, YE Chuan-long, ZHAO Gang, ZHANG Yun-xiang, SONG Ping, SU Yi, CHEN Liang, CENG Ping. STUDY ON STATIC RECRYSTALLIZATION DEVELOPMENT AND MODEL IN HOT ROLLED Nb-Ti STEEL[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(1): 25-29.
Citation:
YU Chi-bin, YE Chuan-long, ZHAO Gang, ZHANG Yun-xiang, SONG Ping, SU Yi, CHEN Liang, CENG Ping. STUDY ON STATIC RECRYSTALLIZATION DEVELOPMENT AND MODEL IN HOT ROLLED Nb-Ti STEEL[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(1): 25-29.
The microstructure development of hot rolled Nb-Ti micro-alloying steel was discussed based on the hot state model test. The affect factors of microstructure development were presented. A mathematical model about static recrystallization and microstructure development was founded. The hot state model tests show the prediction results are in agreement with the experiment results. The study method could simulate the static recrystallization behaviors.