YU Chi-bin, YAN Fei, ZHAO Gang, CHEN Liang, SU Yi, HU Min. EFFECT OF AUSTENITE DEFORMATION ON CONTINUOUS COOLING TRANSFORMATION[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(2): 23-26.
Citation:
YU Chi-bin, YAN Fei, ZHAO Gang, CHEN Liang, SU Yi, HU Min. EFFECT OF AUSTENITE DEFORMATION ON CONTINUOUS COOLING TRANSFORMATION[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(2): 23-26.
YU Chi-bin, YAN Fei, ZHAO Gang, CHEN Liang, SU Yi, HU Min. EFFECT OF AUSTENITE DEFORMATION ON CONTINUOUS COOLING TRANSFORMATION[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(2): 23-26.
Citation:
YU Chi-bin, YAN Fei, ZHAO Gang, CHEN Liang, SU Yi, HU Min. EFFECT OF AUSTENITE DEFORMATION ON CONTINUOUS COOLING TRANSFORMATION[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(2): 23-26.
Applying a THERMECMASTOR-Z hot simulator,the austenite deformation on high temperature and the characteristics of transformarion with continuous cooling were studied for a low carbon Mn-Nb-T microalloyed steel.The dynamic CCT diagram of the steel is established under the deformation conditions.The results indicate that the recrystallization temperature of the steel is 950~980 ℃.The increase of cumulative deformation under recrystallization temperature causes the transformation temperature rising at same cooling rate after the deformation.The recrysallization temperature decreases along with the cooling rate increase.