SONG Li-qiu, HOU Huo-ran, TANG Li, LIU Qing-you, CHENG Xing-de, ZHANG Kai-jian, DONG Han. RESEARCH ON MECHANICAL PROPERTIES OF ULTRA-FINE GRAIN STEEL[J]. IRON STEEL VANADIUM TITANIUM, 2003, 24(4): 1-5.
Citation:
SONG Li-qiu, HOU Huo-ran, TANG Li, LIU Qing-you, CHENG Xing-de, ZHANG Kai-jian, DONG Han. RESEARCH ON MECHANICAL PROPERTIES OF ULTRA-FINE GRAIN STEEL[J]. IRON STEEL VANADIUM TITANIUM, 2003, 24(4): 1-5.
SONG Li-qiu, HOU Huo-ran, TANG Li, LIU Qing-you, CHENG Xing-de, ZHANG Kai-jian, DONG Han. RESEARCH ON MECHANICAL PROPERTIES OF ULTRA-FINE GRAIN STEEL[J]. IRON STEEL VANADIUM TITANIUM, 2003, 24(4): 1-5.
Citation:
SONG Li-qiu, HOU Huo-ran, TANG Li, LIU Qing-you, CHENG Xing-de, ZHANG Kai-jian, DONG Han. RESEARCH ON MECHANICAL PROPERTIES OF ULTRA-FINE GRAIN STEEL[J]. IRON STEEL VANADIUM TITANIUM, 2003, 24(4): 1-5.
Ultra-fine grain hot rolled sheets were produced in 1450 hot mill at PZH Steel, its composition is the same as Q235. The microstructures of ultra-fine grain steel are ferrite and pearlite. Ferrite grain size is about 4 μm. The tensile strength and yield strength of hot rolled sheets are over 510 MPa and 400 MPa respectively. The anisotropy of ultra-fine grain hot rolled sheet is slight. Inclusions are dispersed in steel, so the steel sheet is of good cold-bending property.