Fu Hanguang, Wen Mengxin, Yang Zhijun. APPLICATION OF COMPOSITE MODIFIED HIGH CHROMIUM CAST IRON TO COLD ORE SIEVE PLATE[J]. IRON STEEL VANADIUM TITANIUM, 1997, 18(1): 22-26.
Citation:
Fu Hanguang, Wen Mengxin, Yang Zhijun. APPLICATION OF COMPOSITE MODIFIED HIGH CHROMIUM CAST IRON TO COLD ORE SIEVE PLATE[J]. IRON STEEL VANADIUM TITANIUM, 1997, 18(1): 22-26.
Fu Hanguang, Wen Mengxin, Yang Zhijun. APPLICATION OF COMPOSITE MODIFIED HIGH CHROMIUM CAST IRON TO COLD ORE SIEVE PLATE[J]. IRON STEEL VANADIUM TITANIUM, 1997, 18(1): 22-26.
Citation:
Fu Hanguang, Wen Mengxin, Yang Zhijun. APPLICATION OF COMPOSITE MODIFIED HIGH CHROMIUM CAST IRON TO COLD ORE SIEVE PLATE[J]. IRON STEEL VANADIUM TITANIUM, 1997, 18(1): 22-26.
With a review to the fact that domestic cold ore sieve plates are generally made of CrMnN heat-resisting steel, which has a short service life and freguent replacement, new sieve plates with wear-resisting high Cr cast iron containing K and rare earth have been developed. The installed application has shown that this sort of sieve plate has a better result in safety and reliability,the application of which is worth spreading.