XIAO Feng, XU Chushao, WU Bing, ZHAO Kewen, ZHAO Rongjie. THE INFLUENCE OF VANADIUM ON THERMOPLASTICITY OF STEEL AT TEMPERATURES RANGING FROM 700 TO 1200℃[J]. IRON STEEL VANADIUM TITANIUM, 1998, 19(3): 1-6,19.
Citation:
XIAO Feng, XU Chushao, WU Bing, ZHAO Kewen, ZHAO Rongjie. THE INFLUENCE OF VANADIUM ON THERMOPLASTICITY OF STEEL AT TEMPERATURES RANGING FROM 700 TO 1200℃[J]. IRON STEEL VANADIUM TITANIUM, 1998, 19(3): 1-6,19.
XIAO Feng, XU Chushao, WU Bing, ZHAO Kewen, ZHAO Rongjie. THE INFLUENCE OF VANADIUM ON THERMOPLASTICITY OF STEEL AT TEMPERATURES RANGING FROM 700 TO 1200℃[J]. IRON STEEL VANADIUM TITANIUM, 1998, 19(3): 1-6,19.
Citation:
XIAO Feng, XU Chushao, WU Bing, ZHAO Kewen, ZHAO Rongjie. THE INFLUENCE OF VANADIUM ON THERMOPLASTICITY OF STEEL AT TEMPERATURES RANGING FROM 700 TO 1200℃[J]. IRON STEEL VANADIUM TITANIUM, 1998, 19(3): 1-6,19.
Thermoplasticity of vanadium steel and vanadium-free steel was measured on GLEEBLE-1500 thermal-mechanical simulator. The morphology of vanadium in steel under different conditions at temperatures ranging from 700 to 1200℃ and its influence on thermoplasticlty of steel were studied.