Yu Zisu, Wang Gong, Luo Chuanyue, Chen Wan'an. DEVELOPMENT OF LINING PLATES OF HIGH CIHROMIUM CAST IRON CONTAINING V[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(1): 38-43,48.
Citation:
Yu Zisu, Wang Gong, Luo Chuanyue, Chen Wan'an. DEVELOPMENT OF LINING PLATES OF HIGH CIHROMIUM CAST IRON CONTAINING V[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(1): 38-43,48.
Yu Zisu, Wang Gong, Luo Chuanyue, Chen Wan'an. DEVELOPMENT OF LINING PLATES OF HIGH CIHROMIUM CAST IRON CONTAINING V[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(1): 38-43,48.
Citation:
Yu Zisu, Wang Gong, Luo Chuanyue, Chen Wan'an. DEVELOPMENT OF LINING PLATES OF HIGH CIHROMIUM CAST IRON CONTAINING V[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(1): 38-43,48.
This paper investigates the characteristics of KmTBCr15WVTi cast iron which is produced using as-cast fast cooling and the effects of V content on its microstructure, mechanical properties and wear resistance. The results obtained show that the service life of sinter machine lining plates made of this material is 4 to 6 times longer than that of 2G50Mn2CrMoV in room temperature. Better economical benifit has been gained.