HUANG Xu, CHEN Jie, YAO Yongguo, DONG Jun, HE Qiping, LEI Xiuhua. EFFECT OF H2S ON CORROSION BEHAVIOR OF LOW CARBON STEEL IN COKE OVEN GAS[J]. IRON STEEL VANADIUM TITANIUM, 1998, 19(4): 14-20.
Citation:
HUANG Xu, CHEN Jie, YAO Yongguo, DONG Jun, HE Qiping, LEI Xiuhua. EFFECT OF H2S ON CORROSION BEHAVIOR OF LOW CARBON STEEL IN COKE OVEN GAS[J]. IRON STEEL VANADIUM TITANIUM, 1998, 19(4): 14-20.
HUANG Xu, CHEN Jie, YAO Yongguo, DONG Jun, HE Qiping, LEI Xiuhua. EFFECT OF H2S ON CORROSION BEHAVIOR OF LOW CARBON STEEL IN COKE OVEN GAS[J]. IRON STEEL VANADIUM TITANIUM, 1998, 19(4): 14-20.
Citation:
HUANG Xu, CHEN Jie, YAO Yongguo, DONG Jun, HE Qiping, LEI Xiuhua. EFFECT OF H2S ON CORROSION BEHAVIOR OF LOW CARBON STEEL IN COKE OVEN GAS[J]. IRON STEEL VANADIUM TITANIUM, 1998, 19(4): 14-20.
The effect of H2 on the corrosion dynamics of low carbon steel in coke oven gas was investigated. It is showed that the electropolar process controlling step changes remarkably at 0.15g/m3 H2,corrosion controlling step is cathodic reactions at<0.15g/m3 H2 and anodic reactions at>0.15g/m3H2.There is evidence that the dense protective film forms on the surface of low carbon steel in high H2 coke oven gas. The phenomena are theoretically explained.